PRODUCT |
IN CAST-40 |
IN CAST-70 |
IN CAST-90 |
IN CAST-110 |
IN CAST-130 |
IN CAST-150 |
IN CAST-11 L.I |
IN CAST-13 L.I |
Nature Of Bond Installation |
Hydraulic Temping |
Hydraulic Temping |
Hydraulic Temping |
Hydraulic Temping |
Hydraulic Temping |
Hydraulic Temping |
Hydraulic Temping |
Hydraulic Temping |
Maximum Service Temperature |
1000°C |
1100°C |
1200°C |
1300°C |
1350°C |
1350°C |
1350°C |
1400°C |
Water Required For Casting |
80-100% |
60-65% |
38-43% |
29-34% |
26-31% |
23-28% |
30-35% |
30-35% |
Maximum Grain Size |
6 mm |
6 mm |
6 mm |
6 mm |
6 mm |
6 mm |
6 mm |
6 mm |
CHEMICAL PROPERTIES |
||||||||
Al₂O₃ (Min) |
– |
– |
– |
– |
– |
– |
43.00 |
44.50 |
Fe2O3 (Max) |
11.00 |
8.50 |
6.00 |
3.50 |
3.50 |
3.20 |
1.50 |
1.50 |
PHYSICAL PROPERTES |
||||||||
Dry Density gms/cc at 110°C/24hrs. (Max) |
0.55 |
0.85 |
1 |
1.25 |
1.45 |
1.6 |
1.25 |
1.45 |
C.C.S. (kg/ cm²) At 110°C/24hrs (Min) |
4 |
12 |
15 |
35 |
50 |
90 |
45 |
50 |
At 800°C/3hrs (Min) |
– |
4 |
6 |
25 |
30 |
60 |
– |
– |
At 1100°C/3hrs (Min) |
– |
6 |
– |
25 |
30 |
60 |
30 |
30 |
At 1200°C/3hrs (Min) |
– |
– |
10 |
– |
– |
– |
– |
– |
At 1300°C/3hrs (Min) |
– |
– |
– |
40 |
50 |
70 |
– |
– |
At Service Temperature (Min) |
2 |
– |
– |
– |
– |
– |
50 |
50 |
% Retained On Max Size (Max) |
– |
5 |
5 |
5 |
5 |
5 |
– |
– |
THERMAL PROPERTIES |
||||||||
Refractoriness (O.C./°C) (Min) |
– |
12/1337 |
14/1398 |
14/1398 |
15/1430 |
14/1398 |
15/1430 |
– |
P.L.C. % At 500°C/3hrs (Max) |
– |
– |
– |
– |
– |
– |
– |
– |
At 800°C/3hrs (Max) |
+/-0.40 |
+/-0.80 |
+/-0.60 |
– |
– |
– |
– |
– |
At 1100°C/3hrs (Max) |
– |
+/-1.2 |
– |
+/-0.20 |
+/-0.20 |
+/-0.20 |
+/-0.20 |
+/-0.20 |
At 1200°C/3hrs (Max) |
– |
– |
1 |
– |
– |
– |
– |
– |
At 1300°C/3hrs (Max) |
– |
– |
– |
1 |
0.8 |
1 |
– |
– |
At Service Temperature (Max) |
– |
– |
– |
– |
– |
– |
1 |
0.8 |
THERMAL CONDUCTIVITY |
||||||||
Kcal/m/hr/°C 500°C HF (Max) |
0.1 |
0.18 |
0.28 |
0.31 |
0.33 |
0.44 |
0.34 |
0.4 |
NOTE:
C.C.S. % P.L.C. Values Are On 4 x 4 x 16 cm, PRISMS.
Thermal Conductivity Preferred Hot Face 500°C.
The Above Data Represents Average Test Values Subject To Reasonable Variations.
Delivery: Dry State.