SR NO. |
PRODUCTS |
Al₂O₃% (Min) |
Fe2O3% (Max) |
A.P.% (Max) |
B.D. (Gm/cc) |
C.C.S. (kgf/cm2) |
P.C.E(O.C.)°C (Min) |
R.U.LTa°C (Min) |
P.L.C % (Max) |
APPLICATIONS |
|
1 |
40 |
40 |
2.50 |
22 |
2.20 |
400 |
32/1717 |
1420 |
+/-1.0 at 1450°C/2hrs |
General Purpose Bauxite Based Bricks. |
|
2 |
45-D |
45 |
2.0 |
20 |
2.25 |
450 |
33/1743 |
1450 |
+/-1.0 at 1450°C/2hrs |
Dense High Abrasion Resistance High Volume Stability At Elevated Temp. |
|
3 |
50 |
50 |
2.80 |
23 |
2.30 |
400 |
32.5/1724 |
1400 |
+/-1.0 at 1450°C/2hrs |
High Alumina Bricks Suitable For Cement Rotary Kiln, Ladle Lining. |
|
4 |
55 |
55 |
3.0 |
23 |
2.40 |
400 |
33/1743 |
1430 |
+/-1.5 at 1450°C/2hrs |
High Alumina Bricks Suitable For Cement Rotary Kiln, Ladle Lining. |
|
5 |
60 |
60 |
3.0 |
23 |
2.45 |
400 |
34/1763 |
1440 |
+/- 2.0 at 1500°C/2hrs
|
High Alumina Bricks Suitable For Cement Rotary Kiln, Ladle Lining. |
|
6 |
62-D |
62 |
2.0 |
18 |
2.60 |
700 |
36/1804 |
1500 |
+/- 1.0 at 1500°C/2hrs |
Blast Furnace Stoves & Checkers. |
|
7 |
70 |
70 |
3.20 |
22 |
2.65 |
500 |
35/1785 |
1450 |
+/- 2.0 at 1500°C/2hrs
|
High Alumina Bricks Resistance To Alkali Slag Attack, Suitable For Burning Zone Of Cement Rotary Kiln, Ladle Lining. |
|
8 |
80 |
80 |
2.50 |
21 |
2.75 |
600 |
37/1820 |
1480 |
+/- 2.5 at 1500°C/2hrs |
High Alumina Bricks Suitable For High Temp.Kiln. Soaking Pit Walls, Electric Furnace Roof. |
Note:
Size Tolerance +/-1.5% or 2mm Whichever Is Greater.
The Above Data Are Pertaining To Average Test Values Of Machine pressed Standard Bricks.